Representing the casing and tubing to be used in frigid zones, this series is designed with increased resistance for low-temperature impact in order to withstand shock during delivery, handling, storage, make up, and running in frigid zones. Quenching and tempering is performed to ensure both high yield strength and good low-temperature toughness. Note that the Charpy impact test data of 新澳门六合彩投注-125L with heavy wall of 0.725 in. below show good results at – 50 F. Tensile test results and variation of HRC also show good properties.
Seamless, quenched and tempered
Grade | Tensile Requirements | 2mm V Charpy Impact Requirements (casing only) | |||||
---|---|---|---|---|---|---|---|
Yield Strength ksi (MPa) |
Tensile Strength min. ksi (MPa) |
Elongation | Test Temperature |
Specimen | Minimum Average Absorbed Energy ft-lb (J) | Minimum Individual Absorbed Energy ft-lb (J) |
|
新澳门六合彩投注-80L | 80~95 (552~655) |
95 (655) | As Per API 5CT |
-50 °F (-46 °C) |
10x10 | 25 (34) | 19 (26) |
新澳门六合彩投注-95L | 95~125 (655~862) |
110 (758) | |||||
10x7.5 | 20 (27) | 15 (20) | |||||
新澳门六合彩投注-110L | 110~140 (758~965) |
125 (862) | |||||
10x5 | 14 (19) | 10 (14) | |||||
新澳门六合彩投注-125L | 125~150 (862~1034) |
135 (931) |
Variation of HRC among three locations (O.D., Mid wall, I.D.) of one quadrant of a ring from 新澳门六合彩投注-125L shall be as below.
Wall thickness (inch) | Maximum Variation |
---|---|
0.500 or less | 3.0 |
0.501 to 0.749 | 4.0 |
0.750 and above | 5.0 |
Measurements were made on four quadrants of one test ring.
1 | 2 | 3 | 4 | |
---|---|---|---|---|
Outside Mid Wall Inside |
31.3 31.2 31.6 |
30.5 31.3 31.6 |
30.7 31.2 31.7 |
30.8 31.5 31.5 |
Variation | 0.3 | 1.1 | 1.0 | 0.7 |
Specimen : full size (10 x 10)